It seems safe to say that self-healing materials are extremely fascinating. The 3D printing world has shown them increasing interest lately, with potential applications including electronic devices and cartilage replacements. Last summer, a team of researchers at the University of Manitoba created a new method of designing conductive, 3D printable, self-healing hydrogel materials to make them mechanically stable, which involved both physical and chemical cross-linking.
3D hydrogels are hydrophilic polymeric networks cross-linked by either chemical covalent bonds, physical interactions, or a combination of the two. Because of the crosslinks between polymer chains and their hydrophilic nature, hydrogels can actually swell up to a hundred times, or even a thousand, of their dried mass without needing to be dissolved in water.
While hydrogels used to be pre-prepared and implanted into target sites within the human body during surgical procedures, they can now be easily injected from a syringe through a fine needle, making the material perfect for biomedical applications.
According to a dissertation, titled “Injectable Composite Hydrogels Based on Metal-Ligand Assembly for Biomedical Applications,” by Liyang Shi with Uppsala University in Sweden, injectable hydrogels are very useful in developing minimally invasive surgical procedures, as they “avoid damage of surrounding tissues during implantation surgery” and can easily fill defects with complex shapes in situ. In addition, it’s not difficult to 3D print injectable hydrogels so they form more advanced, customized morphology hydrogels by automating their extrusion from a syringe and programming the movement in a CAD file.
The abstract of Shi’s dissertation reads, “This thesis presents new strategies to construct injectable hydrogels and their various biomedical applications, such as 3D printing, regenerative medicine and drug delivery. These hydrogels cross-linked by dynamic metal-ligand coordination bonds exhibit shear-thinning and selfhealing properties, resulting in the unlimited time window for injection. Compared with nondynamic networks based on chemically reactive liquid polymer precursors that forms covalent bond during and/or post-injection, our injectable hydrogels with dynamic cross-linkages can be injected from an already cross-linked hydrogel state.”
Shi used hyaluronic acid (HA) as the polymer, because it is both biocompatible and biodegradable. First, it was modified with bisphosphonate (BP) as chelating (heterocyclic ring-shaped chemical compound) ligand.
“In the first part of this thesis, I presented the different chemical approaches to synthesize BP-modified HA (HA-BP) derivatives as well as HA derivatives dually modified with BP and acrylamide (Am) groups (Am-HA-BP). The structures of HA-BP derivatives were confirmed by NMR characterizations, e.g. by the peak at 2.18 ppm for methylene protons adjacent to the bridging carbon of BP in 1H-NMR spectrum and phosphorus peak at 18.27 ppm in 31P-NMR spectrum, respectively,” Shi continued. “In the next part, the hydrogels were constructed by simple mixing of HA-BP or Am-HA-BP solution with Ca2+ ions (Paper I), Ag+ ions (Paper II), calcium phosphonate coated silk microfibers (CaP@mSF) (Paper III), and magnesium silicate (MgSiO3) nanoparticles (Paper IV).”
The hydrogels created during the experiment “exhibited dynamic features” like shear-thinning and self-healing properties. Shi applied four types of hydrogels based in HA-BP to different biomedical applications, including 3D printing, wound healing, bone regeneration, and controlled delivery of anti-cancer drugs.
“Additionally, reversible coordination hydrogels were demonstrated to be further covalently cross-linked by UV light to form a secondary cross-linkage, allowing an increase of the strength and modulus of the hydrogels,” Shi wrote.” In the last part of this thesis, biomedical applications of these hydrogels were presented.”
Shi used a homemade 3D printer to extrude Am-HA-BP'¢Ca2+ hydrogel, before using UV radiation to create a 3D tube-like construct with multiple layers. Using a rat model with full-thickness skin defects, HA-BP'¢Ag+hydrogel was able to increase the wound healing process, along with the thickness of the rat’s new epidermal layer.
In addition, double cross-linked Am-HA-BP'¢CaP@mSF hydrogel was able to induce new bone to form, without having to add any biological factors or cells. Finally, the hydrogel loaded with anti-cancer drugs was prepared by mixing HA-BP solution with drug-loaded MgSiO3 nanoparticles; the released particles from this combination “were shown to be taken up by cancer cells to induce a toxic response.”
“In summary, this thesis presents metal-ligand coordination chemical strategies to build injectable hydrogels with dynamic cross-linking resulting in time-independent injection behavior. These hydrogels open new possibilities for use in biomedical areas,” Shi concluded.
Discuss this research and other 3D printing topics at 3DPrintBoard.com or share your thoughts below.